Mechanical and Thermal Influences on Microstructural and Mechanical Properties during Process-Integrated Thermomechanically Controlled Forging of Tempering Steel AISI 4140

verfasst von: Bernd Arno Behrens, Kai Brunotte, Tom Petersen, Julian Diefenbach
Abstract: Thermomechanical treatment (TMT) describes the effect of thermal and mechanical conditions on the microstructure of materials during processing and offers possible integration in the forging process. TMT materials exhibit a fine-grained microstructure, leading to excellent mechanical properties. In this study, a two-step TMT upsetting process with intermediate cooling is used to demonstrate possibilities for a process-integrated treatment and corresponding properties. A water–air-based cooling system was designed to adjust different phase configurations by varying the target temperature and cooling rate. Four different thermal processing routes and four combinations of applied plastic strains are investigated in standardized mechanical tests and metallographic analyses. The applied TMT results in a finely structured bainitic microstructure of the investigated tempering steel AISI 4140 (42CrMo4) with different characteristics depending on the forming conditions. It can be shown that the demands of the standard (DIN EN ISO 683) in a quenched and tempered state can be fulfilled by means of appropriate forming conditions. The yield strength can be enhanced up to 1174 MPa while elongation at break is about 12.6% and absorbed impact energy reaches 58.5 J without additional heat treatment when the material is formed after rapid cooling.
Organisationseinheit(en): Institut für Umformtechnik und Umformmaschinen
Typ: Artikel
Journal: MATERIALS
Band: 13
Seiten: 1-13
Anzahl der Seiten: 13
ISSN: 1996-1944
Publikationsdatum: 17.12.2020
Publikationsstatus: Veröffentlicht
Peer-reviewed: Ja
ASJC Scopus Sachgebiete: Allgemeine Materialwissenschaften
Elektronische Version(en): https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7765793/ (Zugang: Offen)
https://doi.org/10.3390/ma13245772 (Zugang: Offen)
: Details im Forschungsportal „Research@Leibniz University“

BibTeX

@article{454bb24bbf4d41378ae087c86ca89403,
title = "Mechanical and Thermal Influences on Microstructural and Mechanical Properties during Process-Integrated Thermomechanically Controlled Forging of Tempering Steel AISI 4140",
abstract = "Thermomechanical treatment (TMT) describes the effect of thermal and mechanical conditions on the microstructure of materials during processing and offers possible integration in the forging process. TMT materials exhibit a fine-grained microstructure, leading to excellent mechanical properties. In this study, a two-step TMT upsetting process with intermediate cooling is used to demonstrate possibilities for a process-integrated treatment and corresponding properties. A water–air-based cooling system was designed to adjust different phase configurations by varying the target temperature and cooling rate. Four different thermal processing routes and four combinations of applied plastic strains are investigated in standardized mechanical tests and metallographic analyses. The applied TMT results in a finely structured bainitic microstructure of the investigated tempering steel AISI 4140 (42CrMo4) with different characteristics depending on the forming conditions. It can be shown that the demands of the standard (DIN EN ISO 683) in a quenched and tempered state can be fulfilled by means of appropriate forming conditions. The yield strength can be enhanced up to 1174 MPa while elongation at break is about 12.6% and absorbed impact energy reaches 58.5 J without additional heat treatment when the material is formed after rapid cooling.",
keywords = "Forging, Mechanical properties, Tempering steel, Thermomechanical treatment",
author = "Behrens, {Bernd Arno} and Kai Brunotte and Tom Petersen and Julian Diefenbach",
note = "Funding Information: Acknowledgments: The results presented in this paper were obtained within the research project “Im-provement and identification of mechanical properties in forged parts by immediate post-forming after hot forging on different temperature levels by influencing microstructure of tempering steel” (359921546). The authors would like to thank the Deutsche Forschungsgemeinschaft (German Research Foundation, DFG) for the financial and organizational support of this project.",
year = "2020",
month = dec,
day = "17",
doi = "10.3390/ma13245772",
language = "English",
volume = "13",
pages = "1--13",
journal = "MATERIALS",
issn = "1996-1944",
publisher = "MDPI AG",
number = "24",
}